Textbook Question
Chapter 8.15, Problem 39AAP
Consider the Cu–Zn phase diagram of Figure 8.26.
- a. What is the maximum solid solubility in weight percent of Zn in Cu in the terminal solid solution α?
- b. Identify the intermediate phases in the Cu–Zn phase diagram.
- c. Identify the three-phase invariant reactions in the Cu–Zn diagram.
- i. Determine the composition and temperature coordinates of the invariant reactions.
- ii. Write the equations for the invariant reactions.
- iii. Name the invariant reactions.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
Referring to Figure 1, please answer the following [NOTE: SHOW YOUR WORK on Figure 1]:a. provide the specific name for the phase boundary lines denoted by A and B.
b. identify the phases present at equilibrium in the phase fields denoted by C, D, and E.
c. identify the specific name for the point denoted by F.
d. What is the maximum solid solubility of Mg in Al? At what temperature does it occur?
e. An Al-Mg alloy (10 wt% Mg, 90 wt% Al) is heated slowly (to insure equilibrium) from a temperature of 200 C: i. At what temperature does the first liquid phase form?
ii. What is the composition of the liquid phase at the temperature in part i.? iii. At what temperature does complete melting (no solid phase remaining) occur? iv. What is the composition of the last solid remaining prior to complete melting?
f. Using the equilibrium phase diagram of Figure 1, identify the phases present, their compositions, and their relative mass fractions at equilibrium for a 70 wt% Mg – 30 wt% Al…
Phase Diagram
A/ The lead and tin are partially dissolved in each other in solid state although they completely dissolved
in liguid state. They form eutectic from solid solutions alfa (a) and beta (B) at alloying composition 62% tin
and 38% lead, the eutectic forming temperature is 184oC. Alfa contained 20% tin dissolved in 80% lead at
1840C while beta consist of lead dissolved in tin at 1840C. If the 100 g of eutectic contained 45.5 g of alfa
at 1840C. The melting temperatures of lead and tin are 3290C and 2320C respectively, and the solubility of
tin and lead in each other's diminished to zero at room temperature. Plot the phase diagram for lead- tin
system label all phases and temperature. Show graphically the temperature of the formation of the first
solid for 42% lead alloy
A. What is the maximum solid solubility of Cu in Ag? At what temperature? Write the Ag-Cu eutectic reaction, indicating the reactant and product phase(s), and the temperature and the composition (as wt% Cu) at which the reaction takes place.
Chapter 8 Solutions
Foundations of Materials Science and Engineering
Ch. 8.15 - Define (a) a phase in a material and (b) a phase...Ch. 8.15 - In the pure water pressure-temperature equilibrium...Ch. 8.15 - How many triple points are there in the pure iron...Ch. 8.15 - Write the equation for the Gibbs phase rule and...Ch. 8.15 - Refer to the pressuretemperature equilibrium phase...Ch. 8.15 - (a) What is a cooling curve? (b) What type of...Ch. 8.15 - Prob. 7KCPCh. 8.15 - What is an alloy? What is the difference between...Ch. 8.15 - Prob. 9KCPCh. 8.15 - What is the significance of the liquidus curve?...
Ch. 8.15 - Prob. 11KCPCh. 8.15 - Prob. 12KCPCh. 8.15 - Prob. 13KCPCh. 8.15 - Describe the mechanism that produces the...Ch. 8.15 - Can coring and surrounding occur in a...Ch. 8.15 - What is a monotectic invariant reaction? How is...Ch. 8.15 - Write equations for the following invariant...Ch. 8.15 - How are eutectic and eutectoid reactions similar?...Ch. 8.15 - Distinguish between (a) a terminal phase and (b)...Ch. 8.15 - Distinguish between (a) an intermediate phase and...Ch. 8.15 - What is the difference between a congruently...Ch. 8.15 - Consider an alloy containing 70 wt% Ni and 30 wt%...Ch. 8.15 - Consider the binary eutectic coppersilver phase...Ch. 8.15 - If 500 g of a 40 wt% Ag60 wt% Cu alloy is slowly...Ch. 8.15 - A lead-tin (PbSn) alloy consists of 60 wt%...Ch. 8.15 - A PbSn alloy (Fig. 8.12) contains 40 wt% and 60...Ch. 8.15 - An alloy of 30 wt% Pb70 wt% Sn is slowly cooled...Ch. 8.15 - Consider the binary peritectic iridiumosmium phase...Ch. 8.15 - Consider the binary peritectic iridiumosmium phase...Ch. 8.15 - Consider the binary peritectic iridiumosmium phase...Ch. 8.15 - In the copperlead (CuPb) system (Fig. 8.24) for an...Ch. 8.15 - For an alloy of Cu70 wt% Pb (Fig. 8.24), determine...Ch. 8.15 - What is the average composition (weight percent)...Ch. 8.15 - Consider an Fe4.2 wt% Ni alloy (Fig. 8.17) that is...Ch. 8.15 - Consider an Fe5.0 wt% Ni alloy (Fig. 8.17) that is...Ch. 8.15 - Determine the weight percent and composition in...Ch. 8.15 - Determine the composition in weight percent of the...Ch. 8.15 - Draw, schematically, the liquidus and the solidus...Ch. 8.15 - Consider the CuZn phase diagram of Figure 8.26. a....Ch. 8.15 - Consider the nickelvanadium phase diagram of...Ch. 8.15 - Consider the titaniumaluminum phase diagram of...Ch. 8.15 - What is the composition of point y in Figure...Ch. 8.15 - In Figure 8.12, determine the degree of freedom,...Ch. 8.15 - The cooling curve of an unknown metal shows a...Ch. 8.15 - In the PbSn phase diagram (Fig. 8.12), answer the...Ch. 8.15 - Based on the CuAg phase diagram in Figure P8.23,...Ch. 8.15 - Based on the PdAg phase diagram in Figure EP 8.3,...Ch. 8.15 - Prob. 49SEPCh. 8.15 - Derive the lever rule for the amount in weight...Ch. 8.15 - Based on the AlNi phase diagram given in Figure...Ch. 8.15 - Prob. 52SEPCh. 8.15 - Based on the Al2O3SiO2 phase diagram in Figure...Ch. 8.15 - (a) Design a CuNi alloy that will be completely...Ch. 8.15 - Prob. 55SEPCh. 8.15 - Given that Pb and Sn have similar tensile...Ch. 8.15 - Consider the sugarwater phase diagram shown in...Ch. 8.15 - In Figure P8.57, if 60 g of water and 140 g of...Ch. 8.15 - In Figure P8.57, if 30 g of water and 170 g of...Ch. 8.15 - At 80C, if the wt% of sugar is 80%, (a) what...Ch. 8.15 - (a) Based on the phase diagram in Figure P8.61,...Ch. 8.15 - Referring to Figure P8.61. explain what happens as...Ch. 8.15 - Referring to Figure P8.61, (a) explain what...Ch. 8.15 - Using Figure P8.40, explain what the phase diagram...Ch. 8.15 - Using Figure P8.40. explain why, according to the...Ch. 8.15 - (a) In the TiAl phase diagram. Figure P8.42, what...Ch. 8.15 - Draw an approximate hypothetical phase diagram for...Ch. 8.15 - Draw the hypothetical phase diagram for a binary...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- In a binary Fe-Fe3C system, what is the transformation that occurs when cooling an austenistic mixture of 2% C by weight from 1100°C to below the eutectoid temperature? What is the microstructure, and how is it formed? What are the concentrations of the total and partial phases? Data: eutectoid temperature: 723 ºC, eutectoid concentration: 0.76% C, limit concentration of ferrite: 0.022%, limit concentration of cementite: 6.7%.arrow_forwardConsider the binary alloy phase diagram shown schematically below. The left-hand side denotes phase a, and the right-hand side the phase ß. The intermediate region is a coexistence regime with both a and ß phases. The three points 1, 2 and 3 in the coexistence region are at 22.8 wt% A, 28.2 wt% A, and 33.7 wt % A respectively. If the points on the phase boundaries L and R are at 20 wt% A and 39 wt % A, respectively, what is the fraction of a phase at 1, 2 and 3? (This question has only one correct answer) T(°C) A-B binary alloy 1400 Coexistence region 3 1 2 1100 B 20 % 40 % Weight % Aarrow_forwardSuppose an alloy consists of a 75 wt% Sn-25 wt% Pb. i. List the phases present in the alloy at 185 °C. ii. Determine the composition of the phases present in (i). iii. Calculate the relative amount of each phase present at 183 °C in terms of the mass fraction. iv. Sketch with labels the microstructure of the alloy at the temperature of 183 °C – ΔΤ.arrow_forward
- Quenching is a process used to preserve at room temperature a phase which exists in equilibrium at high temperature but which would decompose during equilibrium cooling. Explain the basis of this process in the precipitation process and martensitic transformation. Use phase diagrams when necessary.arrow_forwardDetermine the composition of the phases;arrow_forwardA 45 wt% Pb-55 wt% Mg alloy is rapidly quenched to room temperature from an elevated temperature in such a way that the high- temperature microstructure is preserved. This microstructure is found to consist of the a phase and Mg2Pb, having respective mass fractions of 0.65 and 0.35. Determine the approximate temperature from which the alloy was quenched. Use Animated Figure. °℃arrow_forward
- (c) Suppose an alloy consists of a 75 wt% Sn-25 wt% Pb. i. List the phases present in the alloy at 185 °C. ii. Determine the composition of the phases present in (i). Calculate the relative amount of each phase present at 183 °C in terms of the mass iii. fraction. iv. Sketch with labels the microstructure of the alloy at the temperature of 183 °C - AT.arrow_forwardIn the binary phase diagram for the Cu-Ni system in the Figure provided: 1. Draw the microstructures for each point for the alloy upon cooling (A-E) and label ALL phases! 2. What are the compositions (C's) of EVERY phase and the relative phase amounts (W's) for each microstructure A-E? Show all work! T(°C) (liquid) L 20 (a, solid) 30 A BUD E 40 Co OOOOO w 10 50 wt% Ni CL= Ca= CL= Ca= CL= Ca= C₁= Cu= C₁= Ca= WL= Wa= WL= Wα= W₁= W= W₁= Wa= W₁= Wu= A B Earrow_forwardQuestion: Construct the hypothetical phase diagram for metals A and B between room temperature (20°C) and 700°C given the following information: The melting temperature of metal A is 480°C. The maximum solubility of B in A is 4 wt% B, which occurs at 420°C. The solubility of B in A at room temperature is 0 wt% B. One eutectic occurs at 420°C and 18 wt% B–82 wt% A. A second eutectic occurs at 475°C and 42 wt% B–58 wt% A. The intermetallic compound AB exists at a composition of 30 wt% B–70 wt% A, and melts congruently at 525°C. The melting temperature of metal B is 600°C. The maximum solubility of A in B is 13 wt% A, which occurs at 475°C. ● The solubility of A in B at room temperature is 3 wt% A.arrow_forward
- For a Cu-Ag alley of composition 30 wt% Ag 70 wt% Cu and at 775°C do the following:(a) Determine the mass fractions of alfa and beta phases. (b) Determine the mass fractions of primary alfa and eutectic microconstituents. (c) Determine the mass fraction of eutectic alfaarrow_forward(1) Describe what is meant by the term cooling curve when phase diagrams are considered. (ii) Give a thermodynamic interpretation of the terms break and halt. (iii) Sketch an example of a phase diagram for a binary mixture of compounds A and B, which are solids at room temperature. The melting point of A is higher than that of B. The eutectic point is at 80 mol % A. Compound AB melts incongruently. (vi) Sketch a cooling curve at the composition where compound AB is formed.arrow_forwardPhase diagram of lead-tin system is given in the figure below. For the of composition for 80 wt.% Sn-20 wt.% Pb: (a) Draw schematic sketches of the microstructure, (b) calculate the compositions and weight fractions of each phases at 280°C, just above 183°C (T ) and just below 183°C (T). T° C) 300 L (liquid) TL+BB 97.8 200- 18.3 183° С 1 %3D 3D 100- a + B 13 20 100 32 60 80 C, wt% Snarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Intro to Ceramics and Glasses — Lesson 2, Part 1; Author: Ansys Learning;https://www.youtube.com/watch?v=ArDFnBWH-8w;License: Standard Youtube License