A magnesium-lead alloy of mass 6.7 kg consists of a solid a phase that has a composition just slightly below the solubility limit at 300°C (570°F). The magnesium-lead phase diagram is shown in Animated Figure 9.20. (a) What mass of lead is in the alloy? i kg (b) If the alloy is heated to 400°C (750°F), how much more lead may be dissolved in the a phase without exceeding the solubility limit of this phase? kg

A magnesium-lead alloy of mass 6.7 kg consists of a solid a phase that has a composition just slightly below the solubility limit at 300°C (570°F). The magnesium-lead phase diagram is shown in Animated Figure 9.20. (a) What mass of lead is in the alloy? i kg (b) If the alloy is heated to 400°C (750°F), how much more lead may be dissolved in the a phase without exceeding the solubility limit of this phase? kg

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

An alloy consisting of completely soluble cadmium (Cd) and zinc (Zn) in the liquid state, but neither of them dissolves in each other in the solid state. the table shown below shows the solidification temperatures for various alloys of cadmium and zinc. 1. Draw the equilibrium diagram according to the information given and data in the table and indicating all important temperature and phases. 2. Find the percentage of each phases and percentage of constituents of the alloy that contain 60 % Zn and at a temperature 300 °C. 3. Find the melting point for the following alloys 20 % Cd, 80% Cd 4. Draw the internal structure, noting the phases of the following alloys A) 30 % Cd at 290 °C b) 60 % Cd at room temperature. % of Zinc in alloy Start of solidification ("C) End of solidification ("C) 0 10 14 20 30 40 50 60 321 290 266 275 293 310 328 345 70 80 90 100 362 390 401 419 266 266 266 266 266 266 266 266 266 266 266 266
Temperature ("C) Temperature ($1 Consider 1 kg of Copper - Silver alloy (Cu - Ag) containing 75 wt% Ag. The phase diagram of the alloy is shown in the figure below. The alloy is cooled to 778 °C (just below the eutectic temperature). Calculate the mass in kg of the eutectic phase B (phase B that appears during the eutectic reaction) that forms? Composition (at% Ag 20 40 60 100 2200 80 1200 2000 Liquidus 1000 LIquid 1800 Solidus 1600 800 779°C (T 80 91.2 1400 IC. 1200 600 Solvus T000 400 800 200 20 40 80 100 (Cu) Composioon wt A
Question: Construct the hypothetical phase diagram for metals A and B between room temperature (20°C) and 700°C given the following information: The melting temperature of metal A is 480°C. The maximum solubility of B in A is 4 wt% B, which occurs at 420°C. The solubility of B in A at room temperature is 0 wt% B. One eutectic occurs at 420°C and 18 wt% B–82 wt% A. A second eutectic occurs at 475°C and 42 wt% B–58 wt% A. The intermetallic compound AB exists at a composition of 30 wt% B–70 wt% A, and melts congruently at 525°C. The melting temperature of metal B is 600°C. The maximum solubility of A in B is 13 wt% A, which occurs at 475°C. ● The solubility of A in B at room temperature is 3 wt% A.
For alloy of two hypothetical metals A and B, there exist an a, A-rich phase and a B, B-rich phase. For alloys of two different overall compositions at 25°C, the weight fractions of Wa and WB are listed in the table. Determine the solubility limits for both a and B phases at 25°C. Alloy Composition Wa WB 70wt% A-30wt% B 0.78 0.22 35wt% A-65wt% B 0.36 0.64
a. Determine the composition of each phase in a Cu-40% Ni alloy at 1300°C, 1270°C, 1250°C, and 1200°C. b. Calculate the amounts of α and L at 1250°C in the Cu-40% Ni alloy
A 45 wt% Pb-55 wt% Mg alloy is rapidly quenched to room temperature from an elevated temperature in such a way that the high- temperature microstructure is preserved. This microstructure is found to consist of the a phase and Mg2Pb, having respective mass fractions of 0.65 and 0.35. Determine the approximate temperature from which the alloy was quenched. Use Animated Figure. °℃
1000 grams of steel containing 1.5 weight percent carbon is heated to complete melting. After equilibrium is achieved, we slowly cool the alloy. Determine the amount of pure iron or pure carbon we need to add to this 1000 gram alloy if we need to have 100% pearlite at 720C upon slow cooling from complete melt.
A 42 wt% Pb-58 wt% Mg alloy is heated to a temperature within the α + liquid phase region shown in Animated Figure 9.20. If the composition of the α phase is 30 wt% Pb, determine (a) The temperature of the alloy
A lead-tin (Pb-Sn) alloy of composition 30 wt % Sn and 70 wt % Pb is slowly heated from a temperature of 140 OC. Refer to the phase diagram provided in Figure 1 and answer the following. (i) At what temperature does the first liquid phase form? (ii) What is the composition of this liquid phase? (iii) At what temperature does complete melting of the alloy occur? (iv) What is the composition of the last solid remaining prior to complete melting?
Figure below is a binary eutectic copper-silver phase diagram. Consider if 500 grams of an 88 wt% Ag–12 wt% Cu alloy is slowly cooled from 1000oC to 700oC. α-phase is copper-rich solid solution and β-phase is silver-rich solid solution. Density of copper and silver is 8.96 g/cm3 and 10.49 g/cm3 respectively. At 700oC, determine the: 1)composition of the phases present.
A 50 wt% Ni–50 wt% Cu alloy is heated to a temperature within the a liquid-phase region. If the composition of the alpha phase is 58 wt% Ni, determine (b) the composition of the liquid phase in wt% Ni
For alloys of two hypothetical metals A and B, there exists an a, A-rich phase and a b, B-rich phase. From the mass fractions of both phases for two different alloys (given below), which are at the same temperature, determine the composition of the phase boundary (or solubility limit) for the following: Alloy composition Fraction a Phase Fraction b Phase 60wt%A-40wt%B 0.60 0.40 30wt%A-70wt%B 0.12 0.88 a) a Phase = ___________ wt%A b) b Phase = ___________ wt%A