The preexponential and activation energy for the diffusion of chromium in nickel are 1.1 x 10-4 m²/s and 272,000 J/mol, respectively.At what temperature (in "C) will the diffusion coefficient have a value of 1.1 x 10-14 m²/s?i°C

Answered: Image /qna-images/answer/25934c8d-d23e-4d09-9fcc-0f6c886bf8c2.jpg

The preexponential and activation energy for the diffusion of chromium in nickel are 1.1 × 104 m2/s and 272,000 J/mol, respectively. At what temperature (in "C) will the diffusion coefficient have a value of 1.1 x 10-14 m²/s? i °C

The preexponential and activation energy for the diffusion of chromium in nickel are 1.1 × 104 m2/s and 272,000 J/mol, respectively. At what temperature (in "C) will the diffusion coefficient have a value of 1.1 x 10-14 m²/s? i °C

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: Q2) The nearby figure shows a plot of the logarithm (to the base 10) of the diffusion coefficient…

Q: Carbon is allowed to diffuse through a steel plate 11 mm thick. The concentrations of carbon at the…

Q: propeltionl to tor twesity Cherse the nighte 4. answer s. 1Wdich n the folowing statements Blare…

A: solution 4:- Correct options are- option (a) Option (d)

Q: The activation energy for the diffusion of copper in silver is 193,000 J/mol. Calculate the…

Q: why diffusion coefficient of caarbon inBCC and FCC iron at temperature 912 is different?

A: Diffusion coefficient is a measure of the rate of diffusion of mass of a substance through each unit…

Q: The diffusion coefficient of nickel in an austenitic stainless steel is 10-22 m2/s at 500°C and…

A: Given data: T1=500°CD1=10-22 m2/sT2=1000°CD2=10-15 m2/s Need to determine the activation energy for…

Q: temperature and in an atmosphere in which the surface carbon concentration is maintained at 1.10…

A: Diffusion in alloy is the process of atoms from various alloy components transferring between each…

Q: Derive the dynamics of a geometric brownian motion with zero drift and constant diffusion term.

A: Given Geometric brownian motion To find Dynamics equation

Q: The purification of hydrogen gas is possible by diffusion through a thin palladium sheet. Calculate…

A: Given dATA t = 4.3 mm A = .76 m2 T = 500 °C Ca = Position of higher concentration = 4.2 Cb =…

Q: Define the General Heat/Diffusion Equation ?

A: The general heat equation is a multi-dimensional equation or a three-dimensional equation. The three…

Q: Which of the following is NOT TRUE about the diffusion coefficient equation? A. Its value…

Q: The wear resistance of a steel shaft is to be improved by hardening its surface by increasing the…

A: Explanation: Here we have Where: = 0.0025 % by weight of N = 0.45 % by weight…

Q: At what temperature (in Kelvin) will the diffusion coefficient for the diffusion of species A in…

Q: An open tank, 6 mm in diameter, contains 1 mm deep layer of benzene (Mol wt = 78) at its bottom. The…

A: Given:- Pressure of benzene, Pb1=13.15 KN/m2 Atmospheric pressure, Pt=101.3 KN/m2 d=6mm Layer…

Q: Beginning with a differential control volume, derive the diffusion equation, on a molar basis, for…

A: differential equation for species conservation in cartesian coordinate is used to arrive the…

Q: The purification of hydrogen gas is possible by diffusion through a thin palladium sheet. Calculate…

Q: Determine the settling velocity of a unit-density spherical particle of 0.3 micron (µm) diameter at…

Q: Consider the radial diffusion of a gaseous species (A) through the wall of a plastic tube (B), and…

A: following is the answer to the above question-

Q: The figure below shows five different steady-state concentration profiles from five separate tests,…

Q: The steady-state diffusion flux through a metal plate is 7.8x10* kg/m².s at a temperature of 1200…

A: Write the expression of steady diffusion fluxJ=-D∆C∆xAnd we know that D=Do exp-QdRT

Q: Design a spherical tank, with a wall thickness of 2 cm that will assure that no more than 50 kg of…

A: Diffusion is a process that results from the random motion of molecules and results in a net…

Q: Why does diffusion in solids important?

A: Given question Why is diffusion in solids important? This is a question related to mass transfer.…

Q: Consider diffusion of hydrogen through a poly(dimethyl siloxane) (PDMSO) sheet 20 mm thick. If the…

A: Given data Thickness of PDMSO sheet = 20mmPermeability coefficient at 350 K = 1.31 x 10-10 Hydrogen…

Q: The mass diffusion rate dm/dt across a boundary between two different metals is a function of the…

A: Solution:

Q: How is storage modulus and loss modulus relate with diffussivity of a drug molecule pass through a…

A: The Young's modulus is the proportion of the pressure prompted in a material under an applied…

Q: Consider an alloy that is undergoing carburizing process, initially has a uniform carbon…

A: Carburization is the transformation of a low carbon steel into a high carbon steel. This is…

Q: Describe how Henry’s law and Graham’s law relate to the diffusion constants in Fick’s law.

A: Henry's Law: The amount of gas dissolved in a liquid at a given temperature is proportional to the…

Q: A copper–nickel diffusion couple similar to that shown in Figure 5.1a is fashioned. After a 700-h…

A: Given thatCopper-nickel after 700-h heat treatmentat 1100°C the concentration of Cu is 2.5 wt %To…

Q: Gaseous hydrogen at a constant pressure is to flow within the inside of a thin-walled cylindrical…

Q: 3. A BCC iron alloy containing 0.05 wt% C is carburized at 1050°C such that the carbon concentration…

A: (a) Write the given data. cx=0.5% x=2 mm cs=1.5%co=0.05% T=1050°C Here, cx is the carbon percentage…

Q: Q3) The nearby figure shows a plot of the Temperature ("C) logarithm (to the base 10) of the…

Q: A container was found to weight (80.0 g) while evacuated. The container then was filled with oxygen…

A: We assume that ideal gas behavior is observed

Q: Write down the [units] for the following terms: Diffusion coefficient, [D] = ______________…

Q: After entering Cs, C0 and Cx into the LHS of Fick's second law equation, what does erf(z) equal to?…

A: The value of z is written as, Then, Non-steady state diffusion equation, Substitute the given…

Q: I am unsure which R gas constant units to use. I need to convert the (dy/d(ln(C)) units:…

A: Solution:

Q: A diffusion couple of two metals, A and B, was fashioned as shown: biffusion of A atoms A-B alloy…

Q: The diffusivity of aluminum in a commercial aluminum alloy is 10-20 m2/s at 400°C. The activation…

A: Given data: D1=10-20 m2/sT1=400°CQ=195 kJ/molT2=600°C Need to determine the diffusivity at 600°C.

Q: A thin plastic membrane is used to separate helium from a current. gaseous. Under steady-state…

Q: A tanker ship is transporting 0.798 kg/m3 of a rare gas in its tank. After the fill-up, the 1.94 m…

Q: A gas diffuses through the walls of a pyrex tube whose cross-section is shown in the figure. Derive…

A: INTRODUCTION: We will draw the relationship between the rate of diffusion of gas passing through the…

Q: Consider a diffusion couple setup between pure tungsten and a tungsten alloy containing 1 at%…

A: Diffusion is carried out by three mechanism 1) Self Diffusion it means that random movement of atom…

Q: aseous hydrogen weakens the mechanical strength of cast iron. this phenomenon often occurs in cast…

A: CAs=2.2×10-7 mol H atoms/g FeCA=1.76×10-7mol H atoms/g Fe To- Find:- t=?

Q: An Aluminum-Copper alloy initially containing (0.4 wt% Cu) is placed and held in an atmosphere that…

Q: The microstructure of an iron–carbon alloy consists of proeutectoid cementite and pearlite; the mass…

A: Given data: The iron–carbon alloy consists cementite wα=0.22 The iron–carbon alloy consists pearlite…

Q: A gas diffuses through the walls of a pyrex tube whose cross-section is shown in the figure. Derive…

A: INTRODUCTION: In this problem, we will establish a relationship between the diffusion of gas through…

Q: Carbon is allowed to diffuse through a steel plate 11-mm thick. The concentrations of carbon at the…

A: Explanation: To solve the problem we proceed to use the 1 law of diffusion of flow, Here,…

Concept explainers

Atomic diffusion in solids

In material science, diffusion can take place in solid, liquid, and gases. In solids, atomic diffusion can take place with the help of thermally activated and randomly vibrating atoms. The atomic diffusion in solids is complex and very slow in comparison to atomic diffusion in liquids and gases because the interatomic distance between the atoms is smaller in solids as compared to liquids and gases.

Question

The preexponential and activation energy for the diffusion of chromium in nickel are 1.1 x 10-4 m²/s and 272,000 J/mol, respectively.
At what temperature (in "C) will the diffusion coefficient have a value of 1.1 x 10-14 m²/s?
i
°C

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Compare the diffusion coefficients (in cm²/s) of nitrogen in BCC and FCC iron at the allotropic transformation temperature of 912°C. Decc -153606 X Your response differs from the correct answer by more than 10%. Double check your calculations, cm²/s -1976-7 Dicc x Your response differs significantly from the correct answer. Rework your solution from the beginning and check each step carefully. cm2/s
Using the Tabulation of Diffusion Data, answer the following: (a) Calculate the diffusion coefficient for Cu in Al at 520'C. 7.18e-14 m2/s (Use scientific notation.) (b) What time (in h) will be required at 620°C to produce the same diffusion result (in terms of concentration at a specific point) as for 12hat 520 C? i 2.52
Calculate the value of the diffusion coefficient D (in m2/s) at 750°C for the diffusion of some species in a metal; assume that the values of D0 and Qd are 5.6 × 10-5 m2/s and 177 kJ/mol, respectively.
At what temperature (in Kelvin) will the diffusion coefficient for the diffusion of species A in metal B have a value of 5.20 × 10-16 m2/s, assuming values of 1.3 x 10-5 m2/s and 224,000 J/mol for Do and Qa, respectively?
What temperature is required to obtain 0.4%C at a distance of 0.3 mm beneath the surface of a 0.22% C steel in 2h, when 1.1% C is present at the surface? Assume that the iron is FCC. (Please see figure 5.12 below for diffusion coefficient data. Please use your notes for a table of erf() function values Diffusion coefficient D (cm²/s) ܐ ܐ ܐ ܐ 10- 10-5 10- 10-10 10-11 10-12 10-13 10-14 10-15 Temperature (°C) 2000 1500 1200 1000 900 800 700 600 Cin graphite Mg in MgO Ca in Cao Hin FCC iron C in FCC iron Fe in FCC iron Fe in BCC iron H in BCC iron C in BCC iron Fe in FeO 500 5 6 7 8 9 10 11 12 13 104 T(K) Figure 5-12 The diffusion coefficient D as a function of reciprocal temperature for some metals and ceramics. In this Arrhenius plot, D represents the rate of the diffusion process. A steep slope denotes a high activation energy.
Calculate the value of the diffusion coefficient D (in m^2/s) at 694°C for the diffusion of some species in a metal; assume that the values of D0 and Qd are 5.6 x 10^-5 m^2/s and 177 kJ/mol, respectively. R=8.314 J/(mol*K)
The diffusion coefficient for carbon in BCC iron at 400C and 900C is given as 3.80x10-13 and 1.70x-10m2/s respectively. Determine the temperature (in degrees C) at which a specimen of BCC iron has to be carburized for 150 minutes to produce the same diffusion result as at 900C for one hour.
Consider steady 2D diffusion through a funnel. The funnel radius varies linearly with the distance along the funnel axis according to the following formula: rx=r0*(1+x/L). r0 = 1mm, L=1cm.
Rank the magnitudes of the diffusion coefficients from greatest to least for the following systems: N in Fe at 700°C Cr in Fe at 700°C N in Fe at 900°C Cr in Fe at 900°C Now justify this ranking. (Note: Both Fe and Cr have the BCC crystal structure, and the atomic radii for Fe, Cr, and N are 0.124, 0.125, and 0.065 nm, respectively. You may also want to refer to Section 5.4.)
Carbon is being diffused into chromium at 1400 K (1127°C). The diffusion coefficient at this temperature for the system is 6.25 x 10-11 m/s. Based on this information, calculate the diffusion coefficient of carbon in chromium at a temperature 1300 K (827°C). The activation energy for the diffusion of carbon in chromium is 111,000 J/mol.
The diffusion coefficients for species A in metal B are given at two temperatures: D (m²/s) 8.54 x 10-17 8.39× 10-16 i (b) Determine the value of Do. (a) Determine the value of the activation energy Qd (in J/mol). i J/mol i T (°C) (c) What is the magnitude of D at 1190°C? 1020 1290 m²/s (Use scientific notation.) m²/s (Use scientific notation.)
The activation energy for the diffusion of atomic species A in metal B is 103 kJ/mol. Calculate the diffusion coefficient at 842°C, given that the value of D at 1150°C is 6.5 x 10-12 m²/s. i m²/s