Q2c) Listed in the table below is the tensilestress-strain data for different grades of steels.Utilizing the data given answer the three queriesgiven below.Material YieldTensile Strain at Fracture ElasticStrengthStrengthFractureStrengthModulus(MPa)(MPa)(MPa)(GPa)A41014400.63265410В2002200.40105250C8159500.25500610D8006500.14720210EFractures before yielding6505501) Which will experience the greatest percentreduction in area? Why?2) Which is the strongest? Why?3) Which is the stiffest? Why?

a) For material to experience the greatest percentage reduction in the area it should have a higher…

Material Yield Tensile Strain at Fracture Elastic Strength StrengthFractureStrengthModulus (MPa) (MPa) (MPa) (GPa) 410 1440 0.63 265 410 В 200 220 0.40 105 250 C 815 950 0.25 500 610 D 800 650 0.14 720 210 E Fractures before yielding 650 550 1) Which will experience the greatest percent reduction in area? Why? 2) Which is the strongest? Why? 3) Which is the stiffest? Why? A

Material Yield Tensile Strain at Fracture Elastic Strength StrengthFractureStrengthModulus (MPa) (MPa) (MPa) (GPa) 410 1440 0.63 265 410 В 200 220 0.40 105 250 C 815 950 0.25 500 610 D 800 650 0.14 720 210 E Fractures before yielding 650 550 1) Which will experience the greatest percent reduction in area? Why? 2) Which is the strongest? Why? 3) Which is the stiffest? Why? A

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.5P: The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen...

See similar textbooks

Similar questions

A steel alloy specimen having a rectangular cross section of dimensions 19.1 mm x 3.1 mm (0.7520 in. × 0.1220 in.) has the stress-strain behavior shown in the Animated Figure 6.22b. If this specimen is subjected to a tensile force of 98290 N (22100 Ib;) then (a) Determine the amount of elastic strain induced. (b) Determine the amount of plastic strain induced. (c) If its original length is 610 mm, what will be its final length after this force is applied and then released? The elastic modulus for steel is 207 GPa. (a) i (b) i (c) i mm
S Figure P1.16 shows the stress-strain relations of metals A and B during ten- sion tests until fracture. Determine the following for the two metals (show all calculations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 m/m. c. Ultimate strength d. Modulus of resilience e. Toughness f. Which metal is more ductile? Why? 900 Metal A 600 Metal B 300 0.00 0.02 0.04 0.06 0.08 0.10 0.12 0.14 Strain, m/m FIGURE P1.16 Stress, MPa
A tensile test specimen of aluminum alloy having a diameter of 0.5 in. and a gage length of 2 in. was tested to fracture. The complete stress-strain diagram for this specimen is shown below to the left. The small strain portion of this diagram has been enlarged (to the right) to show in more detail the linear portion of the stress-strain diagram. Determine (a) Young's modulus or modulus of elasticity (i.e., the slope of linear portion), (b) yield stress (using the so-called 0.2% offset method from the lecture notes), (c) yield strain (i.e., the strain corresponding to yield stress, not the 0.2%!), (d) ultimate strength (i.e., the peak in stress-strain diagram), (e) rupture stress (i.e., stress at breaking/failure), (f) rupture strain (i.e., the strain corresponding to rupture stress). 80 70 70 60 60 50 50 40 30 30 20 20 10 10 0.005 0.01 0.015 0.02 Strain (in/in) Strain (in/in) Stress (ksi) 0.015 - 0.03 - 0.12 - 0.135 - 0.15 Stress (ksi)
A round steel alloy bar with a diameter of 19 mm and a gauge length of 76 mm was subjected to tension, with the results shown in Table P3.26. Using a computer spreadsheet program, plot the stress-strain relationship. From the graph, determine the Young's modulus of the steel alloy and the deformation corresponding to a 37 kN load. TABLE P3.26 Deformation, Load, kN mm 9 0.0286 18 0.0572 27 0.0859 36 0.1145 45 0.1431 54 0.1718
The information in the photo attached shows elastic properties of a human tibula bone. If you were to take a small cuboidal cross section of the tibula bone and apply the ultimate shear stress, what would be the resulting strain? (a) 1.0 % (b) 6.7 % (c) 10 % (d) 15 % (e) None of the above.
Figure P1.16 shows the stress–strain relations of metals A and B during tension tests until fracture. Determine the following for the two metals (show all calculations and units): Proportional limit Yield stress at an offset strain of 0.002 in./in. Ultimate strength Modulus of resilience Toughness Which metal is more ductile? Why?
1.17 Figure P1.17 shows the stress-strain relations of metals A and B during tension tests until fracture. Determine the following for the two metals (show all calcu- lations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 in./in. 150 - - Metal A 100 • Metal B 50 0.00 0.02 0.04 0.06 0.08 0.10 0.12 0.14 Strain, in./in. FIGURE P1.17 c. Ultimate strength d. Modulus of resilience e. Toughness f. Which metal is more ductile? Why? Stress, ksi
Consider a cylindrical specimen of a steel alloy (Please see the figure) 0.33 in. in diameter and 3.15 inches long that is pulled in tension. given:-Elongation is 0.018 in-Tensile stress = 200 ksi -Tensile strain = 6.83*10^-3 -Ultimate stress = 281.82 ksi -Ultimate strain = 0.05solve: Fracture point (stress and strain values)
Fatigue strength for non- ferrous materials in defined at stress cycles 10^3 10^5 10^7 10^9
Mechanical properties of materials • H.W.: • The following data where obtained during the tensile test of mild steel circular bar 12.75 mm diameter and 203.2 mm gauge length. Determine the following: 1) The apparent stress at each point 2) Strain at each point 3) True stress at each point (Assume D at failure is 8,51 mm and D at max. load is 11.15 mm) 4) Draw stress - strain curved based on: a) Original cross sectional area b) True cross sectional area 5) Proportional limit Mechanical properties of materials 6) Modulus of elasticity 7) Upper and lower yield point 8) Ultimate strength 9) Breaking strength based on the original cross sectional area and on true cross sectional area 10) Percentage of elongation 11) Percentage of reduction in cross sectional area. 12) Ductility, Resilience and toughness Load (N) 4393 16902 29357 33360 33627 35584 41366 48839 52709 55378 56356 43768 Deformation 0.0254 0.127 0.228 0.305 0.356 3.81 6.35 11.68 16.76 26.92 43768 42.42 (mm )
The elastic portion of the tension stress-strain diagram for an aluminum alloy is shown in the figure. The specimen used for the test has a gauge length of 2 in. and a diameter of 0.5 in. If the applied load is 10 kip, determine the new diameter of the specimen. The shear modulus is G al =3.811032 ksi
Stress-strain plot for a metal is given below. Determine the following: a) Modulus of elasticity. b) Yield strength by 0.2% off-set method. c) Tensile and fracture strengths. d) Maximum load that can be sustained by a cylindrical specimen having an original diameter of 15.3 mm. e) If a specimen having an original length of 320 mm and elongation is measured as 2.56 mm, determine the applied stress. 450 400 350 300 250 200 150 100 50 0.002 0.004 0.006 0.008 0.01 0.012 0.014 0.016 Strain Stress (MPa)