Q1/ The table below shows the values of stress amplitude and life cycles :Fatigue strength Sf (Mpa)Number of cycles (Nf)474111417496352300231670652902193026266075The test were done, to estimate the failure, on un-notched axially load specimens under zero mean stress.Calculate a and b using the stress -life equation.

We know that stress life cycle Sf = aNb log Sf = log(a) + n *logN Let us assume Log Sf = Y, log…

Answered: hows the values of stress amplitud…

Engineering

Mechanical Engineering

hows the values of stress amplitud Fatigue strength Sf (Mpa) 474 417

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A material presents S-N fatigue behaviour shown on the right with the fatigue limit being 100 MPa. If a cylindrical bar made from the material has a diameter of 20 mm is subjected to repeated tensile stress along its axis, calculate the maximum allowable tensile load to ensure no occurrence of fatigue failure. Stress amplitude, S Fatigue limit 103 104 105 106 107 Cycles to failure, N (logarithmic scale) 108 10⁹ 1010
Project 3: Table 4 shows the fatigue data of a ductile cast iron to be used for an automobile axle that rotates at an average rotational speed of 750 revolutions per minute: Tuble 4: Fuligue dula of u duclile cust iron Stress Amplitude (МPa) Cycles to Failure 248 1 X 105 236 ЗX 105 224 1X 106 ЗX 106 1 X 107 3 X 107 1 X 108 3 X 108 213 201 193 193 193 a) Make an S-N plot (stress amplitude versus logarithm cycles to failure). b) What is the fatigue limit for this alloy? c) Determine the fatigue lifetimes at stress amplitudes of 230 MPa and 175 MPa? d) Discuss your results.
Table Q4 belowindicates results on a tensile test of a mild steel specimen. 95 kN Proportional Limit load Original diameter Original ga uge length 30 mm 50 mm Yield Point Load 100 kN Extension at proportional limit 0.050 mm Maximum recorded load 160 kN Final length between gauge points 58.8 mm Final minimum diameter 17.9 mm Table Q4 Calculate the following: a. Modulus of Elasticity for the mild steel. b. The proportional limit stress. C. The ultimate tensile strength. d. The percentage elongation. e. The percentage reduction in area.
2-15 Brinell hardness tests were made on a random sample of 10 steel parts during process- ing. The results were Ha values of 230, 232(2), 234, 235(3), 236(2), and 239. Estimate the mean and standard deviation of the ultimate strength in kpsi. Ans: 50.111 kpsi Som- / -1 bpci
Table 4 shows the fatigue data for a ductile cast iron to be used for an automobile axle that rotates at an average rotational speed of 750 revolutions per minute: Table 4: Fatigue data of a ductile cast iron Stress Amplitude Cycles to (MPа) Failure 1 X 105 ЗX 105 1 X 106 3 X 105 1 X 107 ЗX 10 1X 108 248 236 224 213 201 193 193 193 3 X 10$ Make an S-N plot (stress amplitude versus logarithm cycles to failure). What is the fatigue limit for this alloy? Determine the fatigue lifetimes at stress amplitudes of 230 MPa and 175 MPa? Estimate the maximum lifetime of continuous driving that are allowable for the following 250 MPa and 150 MPa stress levels.
a . Sketch stress strain curve if the result shown in table represent the force and extension happened in steel, and show Mechanical properties that we get from tensile test on curve? (10p)Note : Lo=80 mm , Do=10 mm , use excel to plot the curve ExtensionLoad(mm) (N)0 0.900.83 4694.341.67 4831.412.50 4781.083.33 4918.834.17 4926.585.00 5257.075.83 5437.016.66 5575.888.33 5775.189.16 5847.5210.83 5965.4111.67 6010.5312.50 6042.5713.33 6072.2614.16 6092.9315.00 6113.2416.67 6140.3617.50 6146.3718.33 6148.1419.16 6149.1725.00 5940.2125.83 5675.3326.67 4725.52b. What is meant by modulus of rigidity? if it increases what does happen to material? (2p)
Question: 8-2. Determine the material's fatigue properties for the given d... 8-2. Determine the material's fatigue properties for the given data. Shown the plots to obtain the properties. Smooth Specimen-Cyclic Data Plastic Strain Amplitude. Ae./2" Total Strain Stress Amplitude. Reversals to Amplitude. Ac/2 As, Δσ A0/2 (ksi) Failure. 2N, Basquin Equation: 2 2E E 0.0393 0.0393 0.02925 0.01975 0.0196 0.01375 162.5 0.0336 50 162 0.0336 0.0238 68 155 143.5 Δε, 122 = 6,(2N,} Coffin-Manson Equation: 0.0147 256 143.5 0.0145 350 2 136.5 130.5 126.5 121 0.00894 488 0.00521 1,364 1.386 3,540 3.590 9.100 35.200 140.000 0.00980 0.00980 0.00655 0.00630 0.00460 0.00360 0.00295 0.00534 0.00229 0.00211 0.00059 119 Δε Δε, 114 %3D 106 84.5 0.00000 2 2E E 0.00000 Ao All information is given
1 - A tensile test is carried out on a specimen of mild steel of gauge length 40 mm and diameter 7.42 mm. The results are: Load (kN) 10 17 25 30 34 37.5 38.5 36 Extension (mm) 0 0.05 0.08 0.11 0.14 0.20 0.40 0.60 0.90 At fracture the final length of the specimen is 40.90 mm. Plot the load/ extension graph and determine (a) The modulus of elasticity for mild steel, (b) The yield stress, (c) The ultimate tensile strength, (d) The percentage elongation 2 - An aluminum alloy specimen of gauge length 75 mm and of diameter 11.28 mm was subjected to a tensile test, with these results: Load (kN) 2.0 6.5 11.5 13.6 16.0 18.0 19.0 20.5 19.0 Extension (mm) 0 0.012 0.039 0.069 0.080 0.107 0.133 0.158 0.225 0.310 The specimen fractured at a load of 19.0 kN. Determine (a) the modulus of elasticity of the alloy, (b) The percentage elongation. (c) The ductility in term of reduction of area (d) Fracture stress (e) Tensile strength
Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Determine the true stress (in MPa) at yield point. - Determine the true stress (in MPa) at point of ultimate strength. - Determine the true stress (in MPa) at fracture point. - Determine the true strain (in mm/mm) at yield point. (Use at least five decimal units) - Determine the true strain (in mm/mm) at point of ultimate strength. (Use at least five decimal units) - Determine the true strain (in mm/mm) at fracture point. (Use at least five decimal units)
Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. Question 1 ;Determine the elastic energy absorption capacity (in N.mm) of that specimen. Question 2; Determine the plastic energy absorption capacity (in N.mm) of that specimen.
Asiacell 4,ll ON 76% D19:17 سؤال الواجب.docx Problem :- The following data was obtained tensile test on a specimen of 6 mm diameter and gauge length Lo=30 mm: load(KN) 0 40 80 95 90 135 150.2 145 130 120 elongation(mm) 0 0.022 0.13 0.25 0.55 2.01 3.88 4.12 5.22 6 Plot engineering and True (stress-strain) curves, then determine the (oy, ɛy), (ou, ɛu), (of, , ef), ductility , modulus of elasticity . Then select on the drawing (strain hardening (n)), (Necking), (uniform plastic region and non-uniform plastic region) and (elastic & plastic) region)?
Q1- The following data was obtained tensile test ɔn a specimen of 10 mm diameter and gauge length Lo=50 mm: 0 38 | 76.2 92.7 107 149 160.4 | 155 142 124.7 load(KN) | elongation(mm) 0 0.02 0.12 0.25 0.50 2.03 3.55 4.06 5.1 5.84 Using the graphic paper supplied, Plot engineering stress-strain curves, then determine the (ay, ey), (ou , eu), (of,, ef), modulus of elasticity, then detected in the draw ((stroin hardening (m)), (Necking), (uniform plastic region and non-uniform plastic region) and (elastic & plastic) region))?