1- Draw the repeat (mer) unit for the following thermoplastics: PP, PA, PMMA, PTFE, SBS,POM, PEEK, PMMA, PEI and PC.2- A stress of 2500 psi is applied to a polymer serving as a fastener in a complex assembly.At a constant strain, the stress drops to 2400 psi after 100 h. If the stress on the partmust remain above 2100 psi in order for the part to function properly, determine thelife of the assembly.3- List at least 30 thermoplastic materials with name and symbol.4- Draw the repeat (mer) unit for the following thermoplastics: Polyethylene terephthalate(PET), Amine, Bakelite, Epoxy, Phenolic (PF), Polyester, Polyurethane (PUR), and VinylEster.

The repeat unit of PP The repeat unit of PA

Answered: Draw the repeat (mer) unit for the…

Engineering

Mechanical Engineering

Draw the repeat (mer) unit for the following thermoplastics: PP, PA, PMMA, PTFE, SBS,

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

When a viscoelastic material is loaded and unloaded, the unloading curve is different to the loading curve, i.e. it takes more energy to displace the material than it does to return the material to its original configuration. This is known as: Select one: O a. creep O b. stress relaxation O c. hysteresis d. strain-rate dependance
Q2/ Apolmer must not fail when tensile stress of 125 Mpa is applied .if the surfuce energy of this polymer is 0.5 j/ m and modulus of elasticity of 3 Gpa Answer the following : 1. Convert j/m to N/ m 2. Determine the allowable length of crack in ( mm) before failure
Calculate the modulus of rigidity (shear modulus) of an epoxy resin if the modulus of elasticity (Young's modulus) E = 3.5 GPa and the Poisson's ratio = 0.35. Select one: a. G = 2.6 GPa b. G = 10 GPa c. G = 3.15 GPa d. G= 0.1 GPa e. G = 1.3 GPa
Q4:- Compare between thermoplastic and thermosetting polymers.
A composite has 20 vol% fibres with Ef = 150 GPa in a matrix Em = 30 GPa. If subjected to load parallel to the fibre direction, the fibre would fail first when the stress of fibre reaches 22.5 GPa. Note the composite stress is expressed as o̟ = Vf0s, + (1-Vf) omfı. The matrix would fail later at a failure strain of 0.4, where the composite stress is expressed as a, = (1 – V;)ơm- Assume both the matrix and the fibres deform elastically and subsequently undergo brittle fracture. What would be the maximum stress the composite can withstand? 8.1 GPa 4.5 GPa 12 GPa 22.5 GPa 9.6 GPa
STRESS STRAIN Typical for thermosets Typical for thermoplastics Q/Interpret the following drawing
1. An element of graphite-reinforced composite is completely dry and is constrained against any dimensional changes in the 1 and 2 directions, but it is free to expand in the 3 direction. The element absorbs 1.5% of its dry weight in the form of moisture. (a) What is the strain in the 3 direction as a result of the moisture absorption? Why is this strain different from the value given by B3AM? (b) What stresses develop in the element? Assume that moisture absorption does not influence the material properties.
Compression molding is a manufacturing process in which the molding material is preheated then placed in an open mold cavity where the compressive action of the punch forces the polymer into the desired shape as shown in the figure below. Based on your understanding of the behavior of polymers, which of the statements below regarding compression molding of polymers are accurate? Punch Cavity C. -Upper mold half Charge 41 (1) -Lower mold half Knock-out pin V, F |x.F (2) and (3) Molded part a. Lower operating temperatures are more desirable as they reduce viscosity making it easier to fill the cavity b. This process can only be used for thermosets as they can thermally cure from monomer state This process can be used for both thermosets and thermoplastics as they can both be thermally shaped d. This process is suitable for rubber, PVC and polymethyl methacrylate
Find the differences between thermoplastic and thermoset in terms ofi. Recycle abilityii. Hardnessiii. Structureiv. Heating process reaction
A polymer has creep behaviour that can be represented as a power law equation: e = 0 (Jo + Jit") where J, is 0.5 GPa1, J1 is 0.45 GPa's 0.3 and n is 0.3 (with t in seconds). A component of this material has the following applied stress history: There is no stress before t = 0 A positive (tensile) stress of 8 MPa is applied from t = 0 for 4 hours From t = 4 hours to 6 hours, the stress is compressive stress of 2 MPa The stress is then removed. What will the strain in the material be at t = 9 hours? Enter your value as a number to 4 decimal places. You have a 2% error margin with this.
An elastoplastic material with strain hardening has the stress–strain relationshipshown in Figure 1.6(c). The modulus of elasticity is 175 GPa, yield strength is480 MPa, and the slope of the strain-hardening portion of the stress–strain diagramis 20.7 GPa.a. Calculate the strain that corresponds to a stress of 550 MPa.b. If the 550-MPa stress is removed, calculate the permanent strain.
Question 2: [Strain Energy] A composite rod is comprised of an EN8 steel shaft of length, diameter and Young's modulus of 200 mm, 20 mm and 210 GPa, respectively, that is joined end to end to an aluminium shaft of length, diameter and Elastic modulus of 150 mm, 30 mm and 80 GPa, respectively. If the composite rod stores a strain energy of 20 Nm and deforms linear elastically, calculate: The stresses in each rod. The strain energy absorbed by each component shaft. The elongation of the composite rod. The impact load (F) required to induce this strain given the strain energy stored by the composite shaft, if it falls freely through a height (h) of 150 mm.