At an axial load of 24 kN, a 35-mm-wide by 15- mm-thick polyimide polymer bar elongates 3.0 mm while the bar width contracts 0.15 mm. The bar is 230 mm long. At the 24-kN load, the stress in the polymer bar is less than its proportional limit. Determine (a) the modulus of elasticity. (b) Poisson's ratio. (c) the change in the bar thickness.

At an axial load of 24 kN, a 35-mm-wide by 15- mm-thick polyimide polymer bar elongates 3.0 mm while the bar width contracts 0.15 mm. The bar is 230 mm long. At the 24-kN load, the stress in the polymer bar is less than its proportional limit. Determine (a) the modulus of elasticity. (b) Poisson's ratio. (c) the change in the bar thickness.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Q2/ Apolmer must not fail when tensile stress of 125 Mpa is applied .if the surfuce energy of this polymer is 0.5 j/ m and modulus of elasticity of 3 Gpa Answer the following : 1. Convert j/m to N/ m 2. Determine the allowable length of crack in ( mm) before failure
A continuous and aligned fibrous reinforced composite having a cross-sectional area of 975 mm, then the area is subjectedi to an extenal tensile load. If the stresses sustained by the fibre and matrix phases are 215 MPa and 5.38 MPa, respectively, the force sustained by the fibre phase is 76,800 N, and the total longitudinal composite strain is 1.56x103 then determine.
question 1 of 3 A1 meter length of rubber with a Young's modulus of 0.01 GPa, a circular cross-section, and a radius of 0.001 m is subjected to a force of 1,000 N. What is the new length of the rubber after the force is applied (assuming it doesn't break)? O 10.5 m O 32.8 m O 31.8 m O 1.83 m
Calculate the modulus of rigidity (shear modulus) of an epoxy resin if the modulus of elasticity (Young's modulus) E = 3.5 GPa and the Poisson's ratio = 0.35. Select one: a. G = 2.6 GPa b. G = 10 GPa c. G = 3.15 GPa d. G= 0.1 GPa e. G = 1.3 GPa
A polymer sample of height 700 cm with an area of 6 m2 supports a mass of 70 tons. Youngs modulus of the polymer sample is found to be 60 GPa. Calculate the change in height of the polymer sample, applied stress and strain.
At the proportional limit, a 16 mm thick x 69 mm wide bar elongates 6.2 mm under an axial load of 485 kN. The bar is 1.5 m long. If Poisson's ratio is 0.32 for the material, determine the modulus of elasticity (in GPa). Note: Do not include units in your answer. Answer:
A sample of cross-linked natural rubber (polyisoprene) is found to have a shear modulus of 100 kPa at 20˚C. Determine the force needed to stretch a 20 mm diameter by 100 mm long rod to 300 mm (stretched in the length direction). What is the diameter of this rod of natural rubber under such a load?
A tensile force of 200 KN is applied on a 0.02-m diameter and.2-m long rod. After applying the load, the diameter of the rod decreases to 0.01998 m and the length increases to 2.01 m. Assuming no permanent deformation occurs in that material, the modulus of elasticity (GPa) is?
A sample of silicone breast implant, polydimethylsiloxane (PDMS), is placed under unconfined compression. The magnitudes of the resulting longitudinal and transverse strains have been measured to be 2.7 and 1.341, respectively. The young's modulus of the implant is 500 kPa. Calculate the shear and bulk moduli.
A band of polymer is to hold together a bundle of steel rods for up to one year. if the stress on the band is less than 1300 psi, the band will not hold the rods tightly. determine the initial stress that must be applied to the polymer band when it is slipped over the steel. A series of tests showed that an initial stress of 1000 psi decreased to 980 psi after 5 days. (1yr. = 12 mos = 52wks)
A new high stiffness plastic material has a length of 19.7 inches and a thickness of 3 mm and is being considered for use as a bone fixation plate. When subjected to a tensile load of 10000 N, the material stretches to a length of 19.88 inches. Please find the width of this material, which has a modulus of 4 GPa.
A titanium tube with an outside diameter of 25 mm and inside diameter of 20 mm and a length of 200 mm. When an elastic uniaxial tensile force of 30 kN is applied to this tube along its length, what is the final length of that tube? (Modulus of elasticity of Titanium is 105 GPa)