A planned extrusion operation involves cold-rolled steel at 1000°C to diameter of 75 mm with Tength 65 mm and a final length 70 mm Two presses, one with capacity (extrusion force) or 30 MIN and the other with a capacity (extrusion force) of 20 MN, are available for the operation. Is the smaller press sufficient for this operation? K"=35x10*3 N [Hint: Calculate the extrusion force and compare it to the available two presses)

A planned extrusion operation involves cold-rolled steel at 1000°C to diameter of 75 mm with Tength 65 mm and a final length 70 mm Two presses, one with capacity (extrusion force) or 30 MIN and the other with a capacity (extrusion force) of 20 MN, are available for the operation. Is the smaller press sufficient for this operation? K"=35x10*3 N [Hint: Calculate the extrusion force and compare it to the available two presses)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The team is extruding a billet that is 80 mm long with diameter of 40 mm is directly to a diameter of 20 mm. The extrusion die has a die angle of 75°, see Figure 1. For the work metal, K = 600 MPa and n = 0.25. In the Johnson extrusion strain equation, a = 0.8 and b = 1.4. Remaining billet length 75 Ram pressure, p Do Figure 1: Extrusion process. Determine the following design parameters: (a) Extrusion strain (b) Ram pressure at L = 80, 40, and 10 mm. (c) Draw the relationship between the ram pressure and billet length and discuss the results. What are your recommendations to decrease the required ram pressure?
A planned extrusion operation involves cold-rolled steel at 1000°C_with an initial diameter of 110 mmand a final diameter of 20 mm .Two presses, one with capacity (extrusion force) of 20 MN and the other with a capacity (extrusion force) of 7 MN , are available for the operation. Is the smaller press sufficient for this operation? K"=35x10*3 N (Hint: Calculate the extrusion force and compare it to the available two presses]
You have been asked to work on some design problems and technically support the team working on extrusion and forging operations: 1) The team are extruding a billet that is 80 mm long with diameter of 40 mm is directly to a diameter of 20 mm. The extrusion die has a die angle of 75°, see Figure 1. For the work metal, K = 600 MPa and n = 0.25. In the Johnson extrusion strain equation, a = 0.8 and b = 1.4. Remaining billet length 75 Ram pressure, p D. Dr Figure 1: Extrusion process. Determine the following design parameters: (a) Extrusion ratio. (b) True strain (homogeneous deformation). (c) Extrusion strain. (d) Ram pressure at L= 80, 40, and 10 mm. (e) Draw the relationship between the ram pressure and billet length and discuss the results. What are your recommendations to dccrcase the required ram pressure?
A cylindrical 4135 cold-rolled steel workpiece has an upsetting load applied at room temperature using an open-die forging with flat dies to a new height, ha = 50 mm, as shown below. The initial diameter is do = 220 mm, the initial height is ho = 180 mm. 4135 cold-rolled MPa=1100 Psi= 16000 Strain hardening exponent, n = 0.14 A) What is the diameter of the forging at the end of the forging stroke? B) What is the longitudinal true strain of the forging at the end of the forging stroke? C) What is the true (flow) stress required in the material at the end of the forging stroke? D) Using the average pressure formula, what is the corresponding coefficient of friction if the upsetting force at the end of the stroke is 170 MN?
A tube with outer diameter i5mm and inner diameter 10mm, is to be manufactured by direct extrusion. The billet has a diameter of Do and a length of 200mm. The product is extruded at a speed Vf Assume deformation efficiency 80% and material follows O =110(7) N / mm The extrusion pressure and power are 20 MPa and 300KW, respectively. Calculates: c) Extrusion force in KN? d) The speed Vf? e) The tube final length? ) If the power cost is 2 SR/KW.Hr what is the production cost of producing 50 bars having 2-meters length each from the same cross-section?
e) :- An extrusion Process is to Yeduce a 80mm long eylindrical billet from an initial diameter of 5omm to afinal diameter of 15mm.The extrusion die has a die angle 90°. The wor k Malevial has strength čoetficient K=600 MPa, n: 0.25.In the Johnson equation, a = 0.8 and b=1.5 Determine : 1- EXtru sion vatio 2-True strain assuming homogenous deformakion. 3- Ram force. 4. Ram Power if ram speed is 300 mm/min. %3D
A billet 100 mm long and 30 mm in diameter is to be extruded in a direct extrusion operation with extrusion ratio r, = 3.5. The extrudate has a round cross section. The die angle (half angle) = 60°. The work metal has a strength coefficient = 720 MPa, and strain hardening exponent = 0.17. Use the Johnson formula with a = 0.8 andb= 1.2 to estimate extrusion strain. Determine the following: 1. Diameter of the extrudate = mm 2. Butt volume = mm3 3. Actual extrudate length = mm 4. The pressure applied to perform the extrusion process = MPa 5. Ram force = N.
A billet 75mmlong and 25mmin diameter is to be extruded in a direct extrusion operation with extrusion ratio rx = 4.0. The extrudate has a round cross section. The die angle (half angle) = 90° The work metal has a strength coefficient = 415 MPa, and strainhardening exponent = 0.18. Use the Johnson formula with a = 0.8 and b = 1.5 to estimate extrusion strain. Determine the pressure applied to the end of the billet as the ram moves forward
A 3in long and 1in diameter billet is extruded in a direct extrusion operation with an rx = 4.0. The extrusion has a cross section. The angle of the die (half angle) is 90o. The work metal has a resistance coefficient of 60ksi and a strain hardening exponent of 0.18. Use Johnston's formula with a = 0.8 and b = 1.5 to estimate the extrusion stress. Determine the pressure applied to the end of the billet when the piston moves forward.
3) A direct extrusion process is used to reduce a cylindrical part that has a diameter of 5 inch and is 10 inch long to a cylinder with 2 inch diameter. The die angle is 90°. The cylinder material has a strength coefficient of 10 ksi and strain hardening exponent Of 0.15. Determine a. Extrusion strain b. Ram force
During a direct extrusion process for a billet with 5 in long and diameter 2.5 in to 1.6 in. For the work metal, strength coefficient is 75000 Ib/in, and strain hardening exponent is 0.4, also the die angle of extrusion is 90. In Johnson extrusion strain equation a = 0.8, and b= 1.5. Determine: (a) extrusion ratio (b) true strain (c) extrusion strain, and (d) ram pressure at length 5, 4.2, 2.3,1.5,and 0 in.
4.) A sheet-metal part is 2.0 mm thick and 20.0 mm wide. It is bent to an angle 60° and a bend radius 10 mm in a V-die. The metal has a yield strength Sy= 220MPA, Young's modulus of E=200GPA, and a tensile strength SUTS=340 MPa. a.) Determine the bend radius after springback, Rf mm b.) Determine the bend angle after springback, af c.) Compute the required force to bend the part, given that the die opening dimension w=25 mm. (use k=1.3 for V die). F= kN