2: Consider a Cu-80wt% Ni-20% alloy, determine the following: (a) The liquidus and solidus temperature of alloy. (b) The composition of last liquid to solidify. (c) The composition of last solid to melt. (d) The composition of the solid and liquid phases at 1175 °C. (Draw the microstructure at this points) (e) The amount of the solid and liquid phases at 1175 °C.

2: Consider a Cu-80wt% Ni-20% alloy, determine the following: (a) The liquidus and solidus temperature of alloy. (b) The composition of last liquid to solidify. (c) The composition of last solid to melt. (d) The composition of the solid and liquid phases at 1175 °C. (Draw the microstructure at this points) (e) The amount of the solid and liquid phases at 1175 °C.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

1-The microstructural design of Iron-Carbon(Fe-C) alloys has led to the development of vast range of steels for structural material applications. The phase diagram provide means for producing specific microstructures. Using the phase diagram below to answer the following questions A – If the liquid mixture of Fe-3%Wt C is slowly cooled from 1600 C to 1200C indicate the phase(S) that are present at 1200 C . Also calculate the composition of the of phases.(10) B-Describe the sequence of all phase transformation that accour from Fe-1.5%wt C is slowly cooled from 1600 C to 400 C. Use the diagram below to to describe the microstructures for each phase transformation (10)
For 40 wt% Sn – 60 wt% Pb alloy at 150 oC (at point B) as shown in Figure, i. State the name of phase(s) present. ii. Calculate the composition(s) of the phase(s) present. 600 300 Liquid 500 a+L 200 400 300 100 200 100 20 60 100 (Pb) (Sn) Composition (wt % Sn) Temperature ("C) Temperature ("F)
BI (a) Figure BI below shows the equilibrium phase diagram of hypothetical A - B alloy system. Answer the following questions. What are technical names of Line A and Line B? What do they signify? (i) (ii) With the aid sketches, portray the microstructures and phases that are present for the 20wt%A-80wt%B alloy (Alloy A) at the temperatures of 780 °C, 670 °C, 652 °C, and 500 °C, respectively. (iii) Assume an A - B alloy (Alloy B) has 60wt%a - 40wt%L, in terms of weight, at a temperature of 652 °C. Determine the overall composition of Alloy B. (o) emai 700 8 600 500 400 800 0 A 760 °C Line B W a /9.5 20 Line A a + L 650 °C 40 Liquid (L) wt%B Figure B1 52.5 a + ß 60 B+L 80 93.7 B 100 B
Referring to Figure 1, answer the following: What are the liquidus and solidus temperatures for an 80%Pb20%Tl alloy? What is the composition of the solid solution phase for the aforementioned alloy once we hit the liquidus temperature upon cooling? For the same alloy above, use the inverse lever rule to calculate the %solid and %liquid at 325C
Q2: Consider a Cu-80wt% Ni-20% alloy, determine the following: (a) The liquidus and solidus temperature of alloy. (b) The composition of last liquid to solidify. (c) The composition of last solid to melt. (d) The composition of the solid and liquid phases at 1175 °C. (Draw the microstructure at this points) (e) The amount of the solid and liquid phases at 1175 °C. Composition (at% Ni) 0 20 40 60 80 100 1600 T 1500 1400 1300 1200 1100 1000 1085°C 0 (Cu) 20 T Liquid Liquidus line +L 40 60 Composition (wt% Ni) T 1453 C Solidus line 80 رقم الصفحة 1/1 2800 2600 -2400 2200 2000 100 (Ni) Temperature (F)
rams A copper-nickel alloy of composition 75 wt% Ni-25 wt% Cu is slowly heated from a temperature of 1300°C (1573). (a) At what temperature does the first liquid phase form? (b) What is the composition of this liquid phase? T(°C) 1600 (c) At what temperature does complete melting of the alloy occur? (d) What is the composition of the last solid remaining prior to complete melting? 1500 1400 1300 1200 1100 1000 17 / 17 0 L (liquid) 20 liquidus + a solidus 100% 40 α (FCC solid solution) 60 80 100 wt% Ni 17
Q2: Consider a Cu-80wt% Ni-20% alloy, determine the following: (a) The liquidus and solidus temperature of alloy. (b) The composition of last liquid to solidify. (c) The composition of last solid to melt. (d) The composition of the solid and liquid phases at 1175 °C. (Draw the microstructure at this points) (e) The amount of the solid and liquid phases at 1175 °C. Composition at No 1600 2800 1500 2600 1400 2400 1300 1200 2200 1100 2000 1000 0 1085 C 20 Liquid Liquidus line 40 60 Composition (wt% NO 1453 C Solidus line 80 100
A 50 wt% Ni–50 wt% Cu alloy is heated to a temperature within the a liquid-phase region. If the composition of the alpha phase is 58 wt% Ni, determine (b) the composition of the liquid phase in wt% Ni
In the binary phase diagram for the Cu-Ni system in the Figure provided: 1. Draw the microstructures for each point for the alloy upon cooling (A-E) and label ALL phases! 2. What are the compositions (C's) of EVERY phase and the relative phase amounts (W's) for each microstructure A-E? Show all work! TOCL (liquid) 20 (a, solid) 30 A BCD E E 40 OOOOO 50 wt% Ni www CL= Ca= CL= Ca= CL= Ca= CL= Cu= C₁= Ca= W₁= Wa= WL= WQ= W₁= Wa= W₁= Wa= W₁= Wa= A B C D E
A binary alloy having 28 wt% Cu and balance Ag solidifies at 779°C. The solid consists of two phases a and B. Phase a has 9% Cu whereas phase ß has 8 % Ag at 779°C. At room temperature these are pure Ag and Cu respectively Sketch the phase diagram. Label all phases and temperatures. The melting points of copper and silver are 1083 and 9610 respectively s Pà) Estimate the amount of a and B in the above alloy at 779°C and at room temperature.) b) Calculate the mass fraction of phases for 40% Cu alloy at 300 °C and TR c) What is the composition of the alloys in (b)
Draw thermal equilibrium diagram for the binary alloy system (Si-Au), from the following data:- a- Silicon melts at 1414 °C, and gold melts at 1064 °C. b-Eutectic is formed at 360°C containing 20 Wt% Si -80 Wt% Au, and identify all phases are present in the diagram c-Determine the amount of each phase for the alloy which consist of 60 Wt% Si- 40Wt % Au at 1200 °C and 800 °C ,then determine the amount of eutectic at 200 °C?
Using the following table, draw a melting point diagram and estimate the eutectic temperature and composition: Percent composition Melting point range (°C) 100% A 125-126 75% A-25% B 115-120 65% A- 35% B 128-131 50% A- 50% B 135-140 100% B 151-152 Can you suggest what additional points you need to give a more accurate measure of the eutectic point?